01
CTI + dielectric stability
High-voltage tracking
Connectors and breakers need stable insulation under field, pollution and thermal stress.
CTI ≥600V
ELECTRONICS & ELECTRICAL
High-CTI and high-rigidity engineering materials
Connectors, breakers and electrical housings must combine tracking resistance, heat, low absorption and thin-wall flame retardancy.
600V
S265G8 CTI
265°C
HDT @1.8 MPa
200MPa
tensile strength
0.02%
24h water absorption
Operating conditions
Four critical conditions for Electronics & electrical
Each section follows the failure path for this application. Final targets depend on part design, wall thickness and the customer test plan.
02
HDT + creep resistance
Heat and long-term load
Dense electronics near heat sources require rigidity and stable geometry.
HDT 265°C
03
low shrinkage + flow
Thin-wall molding
Connector walls need balanced fill, warpage, weld-line strength and tolerance.
shrinkage 0.2%
04
low absorption
Humidity
PPS and modified PPO provide stable insulation and dimensions in changing humidity.
0.02% / <0.1%
Recommended materials
Recommended grades and data for Electronics & electrical
Data is sourced from product pages and technical documents. The series, suffix, color and thickness must be locked in the controlled TDS.
High-CTI route
S265G8
PPS + 40%GF · Connectors, breakers and rigid structures
Key data
High-CTI route
S265G8
PPS + 40%GF · Connectors, breakers and rigid structures
- CTI
- ≥600V
- Tensile
- 200 MPa
- Flexural modulus
- 13,500 MPa
- HDT
- 265°C @1.8 MPa
- Water absorption
- 0.02% @24h
- Flame
- V-0 @1.6 / 3.2 mm
A black/custom high-rigidity PPS route for harsh electrical environments.
Low-absorption option
PX54F0HR
Modified PPO / PPE · Connectors, 5G and precision electrical
- Flame
- UL94 V-0
- Water absorption
- <0.1%
- Electrical
- low dielectric loss
- Process
- injection / extrusion
Low absorption and dielectric stability suit high-speed connectors and communication structures.
PFAS-free route
CM9610PF
PFAS-free FR PC · FR housings and internal brackets
- Flame
- V-0 @1.5 mm
- System
- halogen- and bromine-free char
- Material
- polycarbonate
- Compliance
- RoHS / REACH / SCIP / UL
For PFAS-free electronics housings and battery-side components, subject to project validation.
S265G8 · Source: content-inventory: S265G8 product page
PX54F0HR · Source: content-inventory: PX54F0HR product page
CM9610PF · Source: content-inventory: CM9610PF product page
Validation & certification
Validate electrical parts from material to assembly
CTI, HDT, water absorption, flame thickness and mechanics must all refer to a specific grade and specimen.
CTI ≥600V
Insulation
Published S265G8 data for high-CTI electrical structures.
HDT 265°C
Heat
At 1.8 MPa and 4 mm; melting point 285°C.
200 MPa
Mechanics
Tensile strength; flexural modulus 13,500 MPa.
1.6 / 3.2 mm
Flame
S265G8 V-0 data; validate against actual wall thickness.
ISO9001:2015IATF16949RoHSREACH
Public data and certificates do not replace project validation. Results apply only to the tested grade, color, thickness, specimen and conditions.
Technical data request
Request the controlled TDS for S265G8
Share the part, operating conditions and targets. A specialist will verify suffix, thickness, regulations and test conditions before sending the document.
Application inquiry
Discuss Electronics & electrical with our team
More complete inputs move the project faster into sample and validation work.
- Voltage and CTI target
- Pitch and wall thickness
- Continuous temperature
- Flame and glow-wire requirement
Need general material guidance or company information?